Twin-roll casting of aluminum-steel clad strips

Research output: Contribution to journalArticleResearchpeer review

Authors

Research Organisations

External Research Organisations

  • Paderborn University
  • National Metallurgical Academy of Ukraine
View graph of relations

Details

Original languageEnglish
Pages (from-to)501-507
Number of pages7
JournalJournal of manufacturing processes
Volume15
Issue number4
Publication statusPublished - 1 Oct 2013

Abstract

The results of experiments on twin-roll casting of aluminum-steel clad strips are presented. For the first time this energy-saving production technology for a clad material of this metals combination was implemented. Besides the experimental equipment and processing details, the results of metallographic, electron microprobe and transmission electron microscopy analysis of the aluminum-steel interface are shown. The pack rolling and deep-drawing tests of the twin-roll cast clad strips were performed to check their applicability for a further processing using plastic deformation. In addition adhesive strength of the bond was tested. The performed analysis have shown the formation of a continuous, thin and uniform layer of intermetallic phases on the materials interface of approx. 3 μm thickness having an adhesive strength over 70 MPa.

Keywords

    Aluminum, Clad interface, Clad strip, Steel, Twin-roll casting

ASJC Scopus subject areas

Cite this

Twin-roll casting of aluminum-steel clad strips. / Grydin, Olexandr; Gerstein, Gregory; Nürnberger, Florian et al.
In: Journal of manufacturing processes, Vol. 15, No. 4, 01.10.2013, p. 501-507.

Research output: Contribution to journalArticleResearchpeer review

Grydin O, Gerstein G, Nürnberger F, Schaper M, Danchenko V. Twin-roll casting of aluminum-steel clad strips. Journal of manufacturing processes. 2013 Oct 1;15(4):501-507. doi: 10.1016/j.jmapro.2013.08.008
Grydin, Olexandr ; Gerstein, Gregory ; Nürnberger, Florian et al. / Twin-roll casting of aluminum-steel clad strips. In: Journal of manufacturing processes. 2013 ; Vol. 15, No. 4. pp. 501-507.
Download
@article{c95f178987064084ae89bb612acde910,
title = "Twin-roll casting of aluminum-steel clad strips",
abstract = "The results of experiments on twin-roll casting of aluminum-steel clad strips are presented. For the first time this energy-saving production technology for a clad material of this metals combination was implemented. Besides the experimental equipment and processing details, the results of metallographic, electron microprobe and transmission electron microscopy analysis of the aluminum-steel interface are shown. The pack rolling and deep-drawing tests of the twin-roll cast clad strips were performed to check their applicability for a further processing using plastic deformation. In addition adhesive strength of the bond was tested. The performed analysis have shown the formation of a continuous, thin and uniform layer of intermetallic phases on the materials interface of approx. 3 μm thickness having an adhesive strength over 70 MPa.",
keywords = "Aluminum, Clad interface, Clad strip, Steel, Twin-roll casting",
author = "Olexandr Grydin and Gregory Gerstein and Florian N{\"u}rnberger and Mirko Schaper and Valentyn Danchenko",
year = "2013",
month = oct,
day = "1",
doi = "10.1016/j.jmapro.2013.08.008",
language = "English",
volume = "15",
pages = "501--507",
journal = "Journal of manufacturing processes",
issn = "1526-6125",
publisher = "Elsevier BV",
number = "4",

}

Download

TY - JOUR

T1 - Twin-roll casting of aluminum-steel clad strips

AU - Grydin, Olexandr

AU - Gerstein, Gregory

AU - Nürnberger, Florian

AU - Schaper, Mirko

AU - Danchenko, Valentyn

PY - 2013/10/1

Y1 - 2013/10/1

N2 - The results of experiments on twin-roll casting of aluminum-steel clad strips are presented. For the first time this energy-saving production technology for a clad material of this metals combination was implemented. Besides the experimental equipment and processing details, the results of metallographic, electron microprobe and transmission electron microscopy analysis of the aluminum-steel interface are shown. The pack rolling and deep-drawing tests of the twin-roll cast clad strips were performed to check their applicability for a further processing using plastic deformation. In addition adhesive strength of the bond was tested. The performed analysis have shown the formation of a continuous, thin and uniform layer of intermetallic phases on the materials interface of approx. 3 μm thickness having an adhesive strength over 70 MPa.

AB - The results of experiments on twin-roll casting of aluminum-steel clad strips are presented. For the first time this energy-saving production technology for a clad material of this metals combination was implemented. Besides the experimental equipment and processing details, the results of metallographic, electron microprobe and transmission electron microscopy analysis of the aluminum-steel interface are shown. The pack rolling and deep-drawing tests of the twin-roll cast clad strips were performed to check their applicability for a further processing using plastic deformation. In addition adhesive strength of the bond was tested. The performed analysis have shown the formation of a continuous, thin and uniform layer of intermetallic phases on the materials interface of approx. 3 μm thickness having an adhesive strength over 70 MPa.

KW - Aluminum

KW - Clad interface

KW - Clad strip

KW - Steel

KW - Twin-roll casting

UR - http://www.scopus.com/inward/record.url?scp=84888003009&partnerID=8YFLogxK

U2 - 10.1016/j.jmapro.2013.08.008

DO - 10.1016/j.jmapro.2013.08.008

M3 - Article

AN - SCOPUS:84888003009

VL - 15

SP - 501

EP - 507

JO - Journal of manufacturing processes

JF - Journal of manufacturing processes

SN - 1526-6125

IS - 4

ER -

By the same author(s)