T1 - Investigation of the relationship between the condensed structure and the chemically bonded water content in the poly(sialate-siloxo) network

AU - Melele, Sorelle J.K.

AU - Tchakouté, Hervé K.

AU - Banenzoué, Charles

AU - Authority, Local Materials

AU - Rüscher, Claus H.

AU - Andreola, Fernanda

AU - Leonelli, Cristina

N1 - © 2018 Elsevier B.V. All rights reserved.

PY - 2018/5

Y1 - 2018/5

N2 - The main objective of this work was to investigate the relationship between the condensed structure and the chemically bonded water content in the metakaolin-based geopolymer network. The kaolin used in this work as an aluminosilicate source was transformed to metakaolin by calcination at 700 °C. The powder of the waste glass and the silica fume were used as silica sources for the synthesis of the hardeners, dissolving with caustic soda solution. The obtained hardeners were characterized by infrared spectroscopy and MAS-NMR 29Si. The metakaolin and the hardeners were used for producing geopolymers cements. The synthesized products were characterized by X-ray diffractometry, infrared spectroscopy, mercury intrusion porosimetry, scanning electron microscopy, MAS-NMR 29Si and 27Al, thermal analyses (TG and DSC) and compressive strength. The results show that the compressive strength of geopolymer cements using hardener from silica fume and the one from waste glass are 61.93 and 25.51 MPa, respectively. The microstructure (SEM observations) of geopolymer cements obtained using hardener from silica fume is homogeneous, compact and dense with an average pore diameter around 13 nm. Whereas, the one obtained using hardener from waste glass are heterogeneous and contains larger pores (with average pore diameter around 168 nm). MAS-NMR 29Si and 27Al results show that the specimen obtained using hardener from the silica fume contains more aluminum in four-fold coordination in its network than the ones using hardener from waste glass. This indicates a higher degree of crosslinking of poly(sialate-siloxo) chains which could lead to a smaller pore sizes and a higher water uptake in the structure of the sample. The amount of chemically bonded water contained in the network of geopolymer cements using hardeners from waste glass and silica fume were 6.82 and 11.23%, respectively, as determined from weight loss in the range 100–300 °C. All these results indicate that the higher content of chemically bonded water in the network of geopolymer cement obtained using hardener from silica fume is related to the much smaller average pore size diameter and the hydrophilic character of aluminum, which reveals obviously better mechanical and microstructural properties of the specimen. This could indicate here a higher degree of condensation using silica fume based hardener for geopolymerization.

AB - The main objective of this work was to investigate the relationship between the condensed structure and the chemically bonded water content in the metakaolin-based geopolymer network. The kaolin used in this work as an aluminosilicate source was transformed to metakaolin by calcination at 700 °C. The powder of the waste glass and the silica fume were used as silica sources for the synthesis of the hardeners, dissolving with caustic soda solution. The obtained hardeners were characterized by infrared spectroscopy and MAS-NMR 29Si. The metakaolin and the hardeners were used for producing geopolymers cements. The synthesized products were characterized by X-ray diffractometry, infrared spectroscopy, mercury intrusion porosimetry, scanning electron microscopy, MAS-NMR 29Si and 27Al, thermal analyses (TG and DSC) and compressive strength. The results show that the compressive strength of geopolymer cements using hardener from silica fume and the one from waste glass are 61.93 and 25.51 MPa, respectively. The microstructure (SEM observations) of geopolymer cements obtained using hardener from silica fume is homogeneous, compact and dense with an average pore diameter around 13 nm. Whereas, the one obtained using hardener from waste glass are heterogeneous and contains larger pores (with average pore diameter around 168 nm). MAS-NMR 29Si and 27Al results show that the specimen obtained using hardener from the silica fume contains more aluminum in four-fold coordination in its network than the ones using hardener from waste glass. This indicates a higher degree of crosslinking of poly(sialate-siloxo) chains which could lead to a smaller pore sizes and a higher water uptake in the structure of the sample. The amount of chemically bonded water contained in the network of geopolymer cements using hardeners from waste glass and silica fume were 6.82 and 11.23%, respectively, as determined from weight loss in the range 100–300 °C. All these results indicate that the higher content of chemically bonded water in the network of geopolymer cement obtained using hardener from silica fume is related to the much smaller average pore size diameter and the hydrophilic character of aluminum, which reveals obviously better mechanical and microstructural properties of the specimen. This could indicate here a higher degree of condensation using silica fume based hardener for geopolymerization.

KW - Chemically bonded water

KW - Compressive strength

KW - Condensed structure

KW - Geopolymer cement

KW - Hardeners

KW - Metakaolin

UR - http://www.scopus.com/inward/record.url?scp=85044283804&partnerID=8YFLogxK

U2 - 10.1016/j.clay.2018.01.029

DO - 10.1016/j.clay.2018.01.029

M3 - Article

AN - SCOPUS:85044283804

VL - 156

SP - 77

EP - 86

JO - Applied clay science

JF - Applied clay science

SN - 0169-1317

ER -