Hydrothermal stability of NaBH4 enclathrated sodalites with aluminosilicate and gallosilicate framework

Research output: Contribution to journalArticleResearchpeer review

Authors

  • Josef Christian Buhl
  • Florian Stemme
  • Irma Poltz

Research Organisations

Details

Original languageEnglish
Pages (from-to)276-282
Number of pages7
JournalMicroporous and Mesoporous Materials
Volume126
Issue number3
Early online date18 Jun 2009
Publication statusPublished - Dec 2009

Abstract

The time dependent stability of tetrahydroborate sodalites with aluminosilicate- and gallosilicate framework was studied in water at room temperature and under hydrothermal conditions at 353 K. The experiments were carried out in different time intervals (4-48 h) using an excess of water according a solid:liquid mass ratio of 1:150. The kinetics of decomposition was followed by registration of weight loss, change of the pH-value and by X-ray powder diffraction as well as FT-IR spectroscopy. Both samples undergo remarkable time dependent decomposition. The decomposition rate is higher for the gallosilicate sodalite even though its crystal size is larger compare to the aluminosilicate sodalite. Besides formation of some X-ray amorphous material in both cases precipitation of crystalline aluminosilicate or gallosilicate was found, always connected with impurities of carbonate anions. FT-IR clearly showed that the remaining parts of sodalite structure of both samples were always pure tetrahydroborate sodalite. No borate species other than BH4- were detected. Thus, hydrolysis of the moisture sensitive BH4- anions by an entrance of water into intact cages can be excluded under the described experimental conditions.

Keywords

    Aluminosilicates, Gallosilicates, Hydrogen storage, Hydrothermal stability, Tetrahydroborate sodalite

ASJC Scopus subject areas

Cite this

Hydrothermal stability of NaBH4 enclathrated sodalites with aluminosilicate and gallosilicate framework. / Buhl, Josef Christian; Stemme, Florian; Poltz, Irma.
In: Microporous and Mesoporous Materials, Vol. 126, No. 3, 12.2009, p. 276-282.

Research output: Contribution to journalArticleResearchpeer review

Buhl JC, Stemme F, Poltz I. Hydrothermal stability of NaBH4 enclathrated sodalites with aluminosilicate and gallosilicate framework. Microporous and Mesoporous Materials. 2009 Dec;126(3):276-282. Epub 2009 Jun 18. doi: 10.1016/j.micromeso.2009.06.018
Buhl, Josef Christian ; Stemme, Florian ; Poltz, Irma. / Hydrothermal stability of NaBH4 enclathrated sodalites with aluminosilicate and gallosilicate framework. In: Microporous and Mesoporous Materials. 2009 ; Vol. 126, No. 3. pp. 276-282.
Download
@article{d9a8a1fc7fad46be85d02645734c7f82,
title = "Hydrothermal stability of NaBH4 enclathrated sodalites with aluminosilicate and gallosilicate framework",
abstract = "The time dependent stability of tetrahydroborate sodalites with aluminosilicate- and gallosilicate framework was studied in water at room temperature and under hydrothermal conditions at 353 K. The experiments were carried out in different time intervals (4-48 h) using an excess of water according a solid:liquid mass ratio of 1:150. The kinetics of decomposition was followed by registration of weight loss, change of the pH-value and by X-ray powder diffraction as well as FT-IR spectroscopy. Both samples undergo remarkable time dependent decomposition. The decomposition rate is higher for the gallosilicate sodalite even though its crystal size is larger compare to the aluminosilicate sodalite. Besides formation of some X-ray amorphous material in both cases precipitation of crystalline aluminosilicate or gallosilicate was found, always connected with impurities of carbonate anions. FT-IR clearly showed that the remaining parts of sodalite structure of both samples were always pure tetrahydroborate sodalite. No borate species other than BH4- were detected. Thus, hydrolysis of the moisture sensitive BH4- anions by an entrance of water into intact cages can be excluded under the described experimental conditions.",
keywords = "Aluminosilicates, Gallosilicates, Hydrogen storage, Hydrothermal stability, Tetrahydroborate sodalite",
author = "Buhl, {Josef Christian} and Florian Stemme and Irma Poltz",
year = "2009",
month = dec,
doi = "10.1016/j.micromeso.2009.06.018",
language = "English",
volume = "126",
pages = "276--282",
journal = "Microporous and Mesoporous Materials",
issn = "1387-1811",
publisher = "Elsevier",
number = "3",

}

Download

TY - JOUR

T1 - Hydrothermal stability of NaBH4 enclathrated sodalites with aluminosilicate and gallosilicate framework

AU - Buhl, Josef Christian

AU - Stemme, Florian

AU - Poltz, Irma

PY - 2009/12

Y1 - 2009/12

N2 - The time dependent stability of tetrahydroborate sodalites with aluminosilicate- and gallosilicate framework was studied in water at room temperature and under hydrothermal conditions at 353 K. The experiments were carried out in different time intervals (4-48 h) using an excess of water according a solid:liquid mass ratio of 1:150. The kinetics of decomposition was followed by registration of weight loss, change of the pH-value and by X-ray powder diffraction as well as FT-IR spectroscopy. Both samples undergo remarkable time dependent decomposition. The decomposition rate is higher for the gallosilicate sodalite even though its crystal size is larger compare to the aluminosilicate sodalite. Besides formation of some X-ray amorphous material in both cases precipitation of crystalline aluminosilicate or gallosilicate was found, always connected with impurities of carbonate anions. FT-IR clearly showed that the remaining parts of sodalite structure of both samples were always pure tetrahydroborate sodalite. No borate species other than BH4- were detected. Thus, hydrolysis of the moisture sensitive BH4- anions by an entrance of water into intact cages can be excluded under the described experimental conditions.

AB - The time dependent stability of tetrahydroborate sodalites with aluminosilicate- and gallosilicate framework was studied in water at room temperature and under hydrothermal conditions at 353 K. The experiments were carried out in different time intervals (4-48 h) using an excess of water according a solid:liquid mass ratio of 1:150. The kinetics of decomposition was followed by registration of weight loss, change of the pH-value and by X-ray powder diffraction as well as FT-IR spectroscopy. Both samples undergo remarkable time dependent decomposition. The decomposition rate is higher for the gallosilicate sodalite even though its crystal size is larger compare to the aluminosilicate sodalite. Besides formation of some X-ray amorphous material in both cases precipitation of crystalline aluminosilicate or gallosilicate was found, always connected with impurities of carbonate anions. FT-IR clearly showed that the remaining parts of sodalite structure of both samples were always pure tetrahydroborate sodalite. No borate species other than BH4- were detected. Thus, hydrolysis of the moisture sensitive BH4- anions by an entrance of water into intact cages can be excluded under the described experimental conditions.

KW - Aluminosilicates

KW - Gallosilicates

KW - Hydrogen storage

KW - Hydrothermal stability

KW - Tetrahydroborate sodalite

UR - http://www.scopus.com/inward/record.url?scp=71749113779&partnerID=8YFLogxK

U2 - 10.1016/j.micromeso.2009.06.018

DO - 10.1016/j.micromeso.2009.06.018

M3 - Article

AN - SCOPUS:71749113779

VL - 126

SP - 276

EP - 282

JO - Microporous and Mesoporous Materials

JF - Microporous and Mesoporous Materials

SN - 1387-1811

IS - 3

ER -