Experimental application of a laser-based manufacturing process to develop a free customizable, scalable thermoelectric generator demonstrated on a hot shaft

Research output: Contribution to journal › Article › Research › peer review

Authors

Research Organisations

External Research Organisations

  • Institut für integrierte Produktion Hannover (IPH)
View graph of relations

Details

Original languageEnglish
Article numbere12590
JournalEngineering Reports
Volume5
Issue number4
Early online date13 Nov 2022
Publication statusPublished - 2 Apr 2023

Abstract

Geometry, design, and processing in addition to the thermoelectric material properties have a significant influence on the economic efficiency and performance of thermoelectric generators (TEGs). While conventional BULK TEGs are elaborate to manufacture and allow only limited variations in geometry, printed TEGs are often restricted in their application and processing temperature due to the use of organic materials. In this work, a proof-of-concept for fabricating modular, customizable, and temperature-stable TEGs is demonstrated by applying an alternative laser process. For this purpose, low temperature cofired ceramics substrates were coated over a large area, freely structured and cut without masks by a laser and sintered to a solid structure in a single optimized thermal post-processing. A scalable design with complex geometry and large cooling surface for application on a hot shaft was realized to prove feasibility. Investigations on sintering characteristics up to a peak temperature of 1173 K, thermoelectric material properties and temperature distribution were carried out for a Ca3Co4O9/Ag-based prototype and evaluated using profilometer, XRD, and IR measurements. For a combined post-processing, an optimal sintering profile could be determined at 1073 K peak temperature with a 20 min holding time. Temperature gradients of up to 100 K could be achieved along a thermocouple. A single TEG module consisting of 12 thermocouples achieved a maximum power of 0.224 μW and open-circuit voltage of 134.41 mV at an average hot-side temperature of 413.6 K and temperature difference of 106.7 K. Three of these modules combined into a common TEG with a total of 36 thermocouples reached a maximum power of 0.58 K and open-circuit voltage of 319.28 mV with a lesser average hot-side temperature of 387.8 K and temperature difference of 83.4 K.

Keywords

    CaCoO, energy harvesting, laser structuring, LTCC, printed ceramics, thermoelectric generator

ASJC Scopus subject areas

Cite this

Experimental application of a laser-based manufacturing process to develop a free customizable, scalable thermoelectric generator demonstrated on a hot shaft. / Abt, Marvin; Kruppa, Katharina; Wolf, Mario et al.
In: Engineering Reports, Vol. 5, No. 4, e12590, 02.04.2023.

Research output: Contribution to journal › Article › Research › peer review

Abt M, Kruppa K, Wolf M, Feldhoff A, Overmeyer L. Experimental application of a laser-based manufacturing process to develop a free customizable, scalable thermoelectric generator demonstrated on a hot shaft. Engineering Reports. 2023 Apr 2;5(4):e12590. Epub 2022 Nov 13. doi: 10.1002/eng2.12590, /10.15488/13364
Abt, Marvin ; Kruppa, Katharina ; Wolf, Mario et al. / Experimental application of a laser-based manufacturing process to develop a free customizable, scalable thermoelectric generator demonstrated on a hot shaft. In: Engineering Reports. 2023 ; Vol. 5, No. 4.
Download
@article{9608e0488d3b4e8096a1be4da8630d1a,
title = "Experimental application of a laser-based manufacturing process to develop a free customizable, scalable thermoelectric generator demonstrated on a hot shaft",
abstract = "Geometry, design, and processing in addition to the thermoelectric material properties have a significant influence on the economic efficiency and performance of thermoelectric generators (TEGs). While conventional BULK TEGs are elaborate to manufacture and allow only limited variations in geometry, printed TEGs are often restricted in their application and processing temperature due to the use of organic materials. In this work, a proof-of-concept for fabricating modular, customizable, and temperature-stable TEGs is demonstrated by applying an alternative laser process. For this purpose, low temperature cofired ceramics substrates were coated over a large area, freely structured and cut without masks by a laser and sintered to a solid structure in a single optimized thermal post-processing. A scalable design with complex geometry and large cooling surface for application on a hot shaft was realized to prove feasibility. Investigations on sintering characteristics up to a peak temperature of 1173 K, thermoelectric material properties and temperature distribution were carried out for a Ca3Co4O9/Ag-based prototype and evaluated using profilometer, XRD, and IR measurements. For a combined post-processing, an optimal sintering profile could be determined at 1073 K peak temperature with a 20 min holding time. Temperature gradients of up to 100 K could be achieved along a thermocouple. A single TEG module consisting of 12 thermocouples achieved a maximum power of 0.224 μW and open-circuit voltage of 134.41 mV at an average hot-side temperature of 413.6 K and temperature difference of 106.7 K. Three of these modules combined into a common TEG with a total of 36 thermocouples reached a maximum power of 0.58 K and open-circuit voltage of 319.28 mV with a lesser average hot-side temperature of 387.8 K and temperature difference of 83.4 K.",
keywords = "CaCoO, energy harvesting, laser structuring, LTCC, printed ceramics, thermoelectric generator",
author = "Marvin Abt and Katharina Kruppa and Mario Wolf and Armin Feldhoff and Ludger Overmeyer",
note = "Funding Information: This work was funded by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) – project number 325156807. Open Access funding enabled and organized by Projekt DEAL. ",
year = "2023",
month = apr,
day = "2",
doi = "10.1002/eng2.12590",
language = "English",
volume = "5",
number = "4",

}

Download

TY - JOUR

T1 - Experimental application of a laser-based manufacturing process to develop a free customizable, scalable thermoelectric generator demonstrated on a hot shaft

AU - Abt, Marvin

AU - Kruppa, Katharina

AU - Wolf, Mario

AU - Feldhoff, Armin

AU - Overmeyer, Ludger

N1 - Funding Information: This work was funded by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) – project number 325156807. Open Access funding enabled and organized by Projekt DEAL.

PY - 2023/4/2

Y1 - 2023/4/2

N2 - Geometry, design, and processing in addition to the thermoelectric material properties have a significant influence on the economic efficiency and performance of thermoelectric generators (TEGs). While conventional BULK TEGs are elaborate to manufacture and allow only limited variations in geometry, printed TEGs are often restricted in their application and processing temperature due to the use of organic materials. In this work, a proof-of-concept for fabricating modular, customizable, and temperature-stable TEGs is demonstrated by applying an alternative laser process. For this purpose, low temperature cofired ceramics substrates were coated over a large area, freely structured and cut without masks by a laser and sintered to a solid structure in a single optimized thermal post-processing. A scalable design with complex geometry and large cooling surface for application on a hot shaft was realized to prove feasibility. Investigations on sintering characteristics up to a peak temperature of 1173 K, thermoelectric material properties and temperature distribution were carried out for a Ca3Co4O9/Ag-based prototype and evaluated using profilometer, XRD, and IR measurements. For a combined post-processing, an optimal sintering profile could be determined at 1073 K peak temperature with a 20 min holding time. Temperature gradients of up to 100 K could be achieved along a thermocouple. A single TEG module consisting of 12 thermocouples achieved a maximum power of 0.224 μW and open-circuit voltage of 134.41 mV at an average hot-side temperature of 413.6 K and temperature difference of 106.7 K. Three of these modules combined into a common TEG with a total of 36 thermocouples reached a maximum power of 0.58 K and open-circuit voltage of 319.28 mV with a lesser average hot-side temperature of 387.8 K and temperature difference of 83.4 K.

AB - Geometry, design, and processing in addition to the thermoelectric material properties have a significant influence on the economic efficiency and performance of thermoelectric generators (TEGs). While conventional BULK TEGs are elaborate to manufacture and allow only limited variations in geometry, printed TEGs are often restricted in their application and processing temperature due to the use of organic materials. In this work, a proof-of-concept for fabricating modular, customizable, and temperature-stable TEGs is demonstrated by applying an alternative laser process. For this purpose, low temperature cofired ceramics substrates were coated over a large area, freely structured and cut without masks by a laser and sintered to a solid structure in a single optimized thermal post-processing. A scalable design with complex geometry and large cooling surface for application on a hot shaft was realized to prove feasibility. Investigations on sintering characteristics up to a peak temperature of 1173 K, thermoelectric material properties and temperature distribution were carried out for a Ca3Co4O9/Ag-based prototype and evaluated using profilometer, XRD, and IR measurements. For a combined post-processing, an optimal sintering profile could be determined at 1073 K peak temperature with a 20 min holding time. Temperature gradients of up to 100 K could be achieved along a thermocouple. A single TEG module consisting of 12 thermocouples achieved a maximum power of 0.224 μW and open-circuit voltage of 134.41 mV at an average hot-side temperature of 413.6 K and temperature difference of 106.7 K. Three of these modules combined into a common TEG with a total of 36 thermocouples reached a maximum power of 0.58 K and open-circuit voltage of 319.28 mV with a lesser average hot-side temperature of 387.8 K and temperature difference of 83.4 K.

KW - CaCoO

KW - energy harvesting

KW - laser structuring

KW - LTCC

KW - printed ceramics

KW - thermoelectric generator

UR - http://www.scopus.com/inward/record.url?scp=85142030263&partnerID=8YFLogxK

U2 - 10.1002/eng2.12590

DO - 10.1002/eng2.12590

M3 - Article

AN - SCOPUS:85142030263

VL - 5

JO - Engineering Reports

JF - Engineering Reports

SN - 2577-8196

IS - 4

M1 - e12590

ER -

By the same author(s)

  1. Advancing oxygen separation: insights from experimental and computational analysis of La0.7Ca0.3Co0.3Fe0.6M0.1O3−δ (M = Cu, Zn) oxygen transport membranes

    Research output: Contribution to journal › Article › Research › peer review

  2. Preparation of ZIF-62 polycrystalline and glass membranes for helium separation

    Research output: Contribution to journal › Article › Research › peer review

  3. Superior Thermoelectric Performance of Textured Ca3Co4−xO9+δ Ceramic Nanoribbons

    Research output: Contribution to journal › Article › Research › peer review

  4. Hydrogen-Tolerant La0.6Ca0.4Co0.2Fe0.8O3–d Oxygen Transport Membranes from Ultrasonic Spray Synthesis for Plasma-Assisted CO2 Conversion

    Research output: Contribution to journal › Article › Research › peer review

  5. Laser generation of CeAlO3 nanocrystals with perovskite structure

    Research output: Contribution to journal › Article › Research › peer review