Details
| Original language | English |
|---|---|
| Pages (from-to) | 143-154 |
| Number of pages | 12 |
| Journal | Materials Science and Engineering A |
| Volume | 396 |
| Issue number | 1-2 |
| Publication status | Published - 15 Apr 2005 |
| Externally published | Yes |
Abstract
We examine the growth of microstructurally small fatigue cracks in cast AM60B magnesium (Mg) cycled in a water vapor environment. The behavior and growth rates of the small cracks were measured in situ during cycling using a fatigue loading stage contained within an environmental scanning electron microscope (ESEM). We provide quantitative data describing the interaction of representative small fatigue cracks with microstructural features, along with the average growth rate data for approximately 20 different cracks. Small surface and corner cracks, with sizes ranging from 20 to 200 μm, are observed to interact strongly with the surface microstructure during growth. The small cracks preferentially propagate through the dendrite cells, and the particle laden interdendritic regions typically act as barriers to fatigue crack propagation. As the small cracks approach the interdendritic boundaries, measured growth rates decrease and the cracks sometimes becomes temporarily pinned at the boundary. Cracks smaller than 100 μm experience more significant disruptions in crack growth rates at interdendritic boundaries compared to the larger cracks that interact with the boundaries, but with less change in crack growth rates. Under nominally identical loading conditions, isolated microstructurally small cracks grow, on average, two orders of magnitude faster in a sample containing a higher fraction of porosity. The significantly higher crack growth rates in the more porous sample were attributed to local amplification of the nominal stress field in the vicinity of the microstructurally small cracks rather than explicit interactions between growing cracks and pores. Analogous to the wrought materials, the growth rate of microstructurally small cracks is observed to be significantly higher compared to long fatigue cracks at equivalent maximum cyclic stress intensity values.
Keywords
- Cast magnesium, Environmental scanning electron microscopy, Fatigue, In situ fatigue, Small cracks
ASJC Scopus subject areas
- Materials Science(all)
- General Materials Science
- Physics and Astronomy(all)
- Condensed Matter Physics
- Engineering(all)
- Mechanics of Materials
- Engineering(all)
- Mechanical Engineering
Cite this
- Standard
- Harvard
- Apa
- Vancouver
- BibTeX
- RIS
In: Materials Science and Engineering A, Vol. 396, No. 1-2, 15.04.2005, p. 143-154.
Research output: Contribution to journal › Article › Research › peer review
}
TY - JOUR
T1 - Environmentally influenced microstructurally small fatigue crack growth in cast magnesium
AU - Gall, Ken
AU - Biallas, Gerhard
AU - Maier, Hans J.
AU - Horstemeyer, Mark F.
AU - McDowell, David L.
N1 - Funding Information: The authors thank Anja Puda for her careful surface preparation of the cast Mg alloy specimens for in situ studies. This work was sponsored by the US Department of Energy under contract DE-AC04-94Al85000, and was performed with the support of Dick Osborne and Don Penrod for the USCAR Lightweight Metals Group. Funding for K. Gall was provided by a DOE PECASE award from Sandia National Laboratories.
PY - 2005/4/15
Y1 - 2005/4/15
N2 - We examine the growth of microstructurally small fatigue cracks in cast AM60B magnesium (Mg) cycled in a water vapor environment. The behavior and growth rates of the small cracks were measured in situ during cycling using a fatigue loading stage contained within an environmental scanning electron microscope (ESEM). We provide quantitative data describing the interaction of representative small fatigue cracks with microstructural features, along with the average growth rate data for approximately 20 different cracks. Small surface and corner cracks, with sizes ranging from 20 to 200 μm, are observed to interact strongly with the surface microstructure during growth. The small cracks preferentially propagate through the dendrite cells, and the particle laden interdendritic regions typically act as barriers to fatigue crack propagation. As the small cracks approach the interdendritic boundaries, measured growth rates decrease and the cracks sometimes becomes temporarily pinned at the boundary. Cracks smaller than 100 μm experience more significant disruptions in crack growth rates at interdendritic boundaries compared to the larger cracks that interact with the boundaries, but with less change in crack growth rates. Under nominally identical loading conditions, isolated microstructurally small cracks grow, on average, two orders of magnitude faster in a sample containing a higher fraction of porosity. The significantly higher crack growth rates in the more porous sample were attributed to local amplification of the nominal stress field in the vicinity of the microstructurally small cracks rather than explicit interactions between growing cracks and pores. Analogous to the wrought materials, the growth rate of microstructurally small cracks is observed to be significantly higher compared to long fatigue cracks at equivalent maximum cyclic stress intensity values.
AB - We examine the growth of microstructurally small fatigue cracks in cast AM60B magnesium (Mg) cycled in a water vapor environment. The behavior and growth rates of the small cracks were measured in situ during cycling using a fatigue loading stage contained within an environmental scanning electron microscope (ESEM). We provide quantitative data describing the interaction of representative small fatigue cracks with microstructural features, along with the average growth rate data for approximately 20 different cracks. Small surface and corner cracks, with sizes ranging from 20 to 200 μm, are observed to interact strongly with the surface microstructure during growth. The small cracks preferentially propagate through the dendrite cells, and the particle laden interdendritic regions typically act as barriers to fatigue crack propagation. As the small cracks approach the interdendritic boundaries, measured growth rates decrease and the cracks sometimes becomes temporarily pinned at the boundary. Cracks smaller than 100 μm experience more significant disruptions in crack growth rates at interdendritic boundaries compared to the larger cracks that interact with the boundaries, but with less change in crack growth rates. Under nominally identical loading conditions, isolated microstructurally small cracks grow, on average, two orders of magnitude faster in a sample containing a higher fraction of porosity. The significantly higher crack growth rates in the more porous sample were attributed to local amplification of the nominal stress field in the vicinity of the microstructurally small cracks rather than explicit interactions between growing cracks and pores. Analogous to the wrought materials, the growth rate of microstructurally small cracks is observed to be significantly higher compared to long fatigue cracks at equivalent maximum cyclic stress intensity values.
KW - Cast magnesium
KW - Environmental scanning electron microscopy
KW - Fatigue
KW - In situ fatigue
KW - Small cracks
UR - http://www.scopus.com/inward/record.url?scp=15944397213&partnerID=8YFLogxK
U2 - 10.1016/j.msea.2005.01.014
DO - 10.1016/j.msea.2005.01.014
M3 - Article
AN - SCOPUS:15944397213
VL - 396
SP - 143
EP - 154
JO - Materials Science and Engineering A
JF - Materials Science and Engineering A
SN - 0921-5093
IS - 1-2
ER -