Characterization of synthetic Cs-Li cancrinite grown in a butanediol-water system: An NMR spectroscopic and Rietveld refinement study

Research output: Contribution to journal › Article › Research › peer review

Authors

  • M. Fechtelkord
  • B. Posnatzki
  • J. C. Buhl
  • C. A. Fyfe
  • L. A. Groat
  • M. Raudsepp

Research Organisations

View graph of relations

Details

Original languageEnglish
Pages (from-to)881-888
Number of pages8
JournalAmerican mineralogist
Volume86
Issue number7-8
Publication statusPublished - 1 Jul 2001

Abstract

A Cs-Li-analogue of cancrinite has been synthesized from tetraethoxysilane and Al sec-butoxide in a mixture of 1,3-butanediol and water. Cs and Li were introduced as hydroxides. Synthesis was done at autogeneous pressure and T = 473 K for 100 h. The synthesis product was characterized by powder X-ray diffraction, IR-spectroscopy, thermogravimetry, 1H, 6Li, 133Cs, 27Al, 29Si MAS, and (1H) 13C CPMAS NMR and Rietveld structure refinement. 29Si MAS NMR and 27Al MAS NMR spectroscopy show a framework with strong alternating order of the SiO4 and AlO4 tetrahedra and an Si/Al ratio of one. 6Li MAS NMR suggests the existence of two different signals that cannot be resolved in the 7Li MAS NMR spectrum. 133Cs MAS NMR shows only a single resonance. The thermogravimetric analysis reveals a continuous weight loss in several steps, indicating the evaporation of water of hydration. IR spectroscopy shows evidence for hydroxyl anions and water included in the cancrinite framework. The Rietveld structure refinement is consistent with a completely ordered alumosilicate framework with an Si/Al ratio of one and the presence of both molecular water and hydroxyl groups in the hexagonal channel, a result different from the previously published structure. Cs is exclusively located in the ε-cages; Li ions are located in the channels and are coordinated by water molecules.

ASJC Scopus subject areas

Cite this

Characterization of synthetic Cs-Li cancrinite grown in a butanediol-water system: An NMR spectroscopic and Rietveld refinement study. / Fechtelkord, M.; Posnatzki, B.; Buhl, J. C. et al.
In: American mineralogist, Vol. 86, No. 7-8, 01.07.2001, p. 881-888.

Research output: Contribution to journal › Article › Research › peer review

Fechtelkord M, Posnatzki B, Buhl JC, Fyfe CA, Groat LA, Raudsepp M. Characterization of synthetic Cs-Li cancrinite grown in a butanediol-water system: An NMR spectroscopic and Rietveld refinement study. American mineralogist. 2001 Jul 1;86(7-8):881-888. doi: 10.2138/am-2001-0711
Download
@article{7827acfafa9045c080df4890a22b694a,
title = "Characterization of synthetic Cs-Li cancrinite grown in a butanediol-water system: An NMR spectroscopic and Rietveld refinement study",
abstract = "A Cs-Li-analogue of cancrinite has been synthesized from tetraethoxysilane and Al sec-butoxide in a mixture of 1,3-butanediol and water. Cs and Li were introduced as hydroxides. Synthesis was done at autogeneous pressure and T = 473 K for 100 h. The synthesis product was characterized by powder X-ray diffraction, IR-spectroscopy, thermogravimetry, 1H, 6Li, 133Cs, 27Al, 29Si MAS, and (1H) 13C CPMAS NMR and Rietveld structure refinement. 29Si MAS NMR and 27Al MAS NMR spectroscopy show a framework with strong alternating order of the SiO4 and AlO4 tetrahedra and an Si/Al ratio of one. 6Li MAS NMR suggests the existence of two different signals that cannot be resolved in the 7Li MAS NMR spectrum. 133Cs MAS NMR shows only a single resonance. The thermogravimetric analysis reveals a continuous weight loss in several steps, indicating the evaporation of water of hydration. IR spectroscopy shows evidence for hydroxyl anions and water included in the cancrinite framework. The Rietveld structure refinement is consistent with a completely ordered alumosilicate framework with an Si/Al ratio of one and the presence of both molecular water and hydroxyl groups in the hexagonal channel, a result different from the previously published structure. Cs is exclusively located in the ε-cages; Li ions are located in the channels and are coordinated by water molecules.",
author = "M. Fechtelkord and B. Posnatzki and Buhl, {J. C.} and Fyfe, {C. A.} and Groat, {L. A.} and M. Raudsepp",
year = "2001",
month = jul,
day = "1",
doi = "10.2138/am-2001-0711",
language = "English",
volume = "86",
pages = "881--888",
journal = "American mineralogist",
issn = "0003-004X",
publisher = "Walter de Gruyter GmbH",
number = "7-8",

}

Download

TY - JOUR

T1 - Characterization of synthetic Cs-Li cancrinite grown in a butanediol-water system

T2 - An NMR spectroscopic and Rietveld refinement study

AU - Fechtelkord, M.

AU - Posnatzki, B.

AU - Buhl, J. C.

AU - Fyfe, C. A.

AU - Groat, L. A.

AU - Raudsepp, M.

PY - 2001/7/1

Y1 - 2001/7/1

N2 - A Cs-Li-analogue of cancrinite has been synthesized from tetraethoxysilane and Al sec-butoxide in a mixture of 1,3-butanediol and water. Cs and Li were introduced as hydroxides. Synthesis was done at autogeneous pressure and T = 473 K for 100 h. The synthesis product was characterized by powder X-ray diffraction, IR-spectroscopy, thermogravimetry, 1H, 6Li, 133Cs, 27Al, 29Si MAS, and (1H) 13C CPMAS NMR and Rietveld structure refinement. 29Si MAS NMR and 27Al MAS NMR spectroscopy show a framework with strong alternating order of the SiO4 and AlO4 tetrahedra and an Si/Al ratio of one. 6Li MAS NMR suggests the existence of two different signals that cannot be resolved in the 7Li MAS NMR spectrum. 133Cs MAS NMR shows only a single resonance. The thermogravimetric analysis reveals a continuous weight loss in several steps, indicating the evaporation of water of hydration. IR spectroscopy shows evidence for hydroxyl anions and water included in the cancrinite framework. The Rietveld structure refinement is consistent with a completely ordered alumosilicate framework with an Si/Al ratio of one and the presence of both molecular water and hydroxyl groups in the hexagonal channel, a result different from the previously published structure. Cs is exclusively located in the ε-cages; Li ions are located in the channels and are coordinated by water molecules.

AB - A Cs-Li-analogue of cancrinite has been synthesized from tetraethoxysilane and Al sec-butoxide in a mixture of 1,3-butanediol and water. Cs and Li were introduced as hydroxides. Synthesis was done at autogeneous pressure and T = 473 K for 100 h. The synthesis product was characterized by powder X-ray diffraction, IR-spectroscopy, thermogravimetry, 1H, 6Li, 133Cs, 27Al, 29Si MAS, and (1H) 13C CPMAS NMR and Rietveld structure refinement. 29Si MAS NMR and 27Al MAS NMR spectroscopy show a framework with strong alternating order of the SiO4 and AlO4 tetrahedra and an Si/Al ratio of one. 6Li MAS NMR suggests the existence of two different signals that cannot be resolved in the 7Li MAS NMR spectrum. 133Cs MAS NMR shows only a single resonance. The thermogravimetric analysis reveals a continuous weight loss in several steps, indicating the evaporation of water of hydration. IR spectroscopy shows evidence for hydroxyl anions and water included in the cancrinite framework. The Rietveld structure refinement is consistent with a completely ordered alumosilicate framework with an Si/Al ratio of one and the presence of both molecular water and hydroxyl groups in the hexagonal channel, a result different from the previously published structure. Cs is exclusively located in the ε-cages; Li ions are located in the channels and are coordinated by water molecules.

UR - http://www.scopus.com/inward/record.url?scp=0034903143&partnerID=8YFLogxK

U2 - 10.2138/am-2001-0711

DO - 10.2138/am-2001-0711

M3 - Article

AN - SCOPUS:0034903143

VL - 86

SP - 881

EP - 888

JO - American mineralogist

JF - American mineralogist

SN - 0003-004X

IS - 7-8

ER -