Thermomechanical Fatigue Behavior of the High-Temperature Titanium Alloy IMI 834

Publikation: Beitrag in FachzeitschriftArtikelForschungPeer-Review

Autoren

Externe Organisationen

  • Universität Siegen
Forschungs-netzwerk anzeigen

Details

OriginalspracheEnglisch
Seiten (von - bis)2995-3004
Seitenumfang10
FachzeitschriftMetallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
Jahrgang29
Ausgabenummer12
PublikationsstatusVeröffentlicht - 1998
Extern publiziertJa

Abstract

The isothermal and thermomechanical fatigue (TMF) behavior of the titanium alloy IMI 834 was studied between 350 °C and 650 °C in air and vacuum, respectively. Transmission electron microscopy (TEM) observations revealed that the microstructure established in the TMF tests was governed by the maximum temperature within the cycle. However, if the maximum temperature does not exceed 600 °C, planar dislocation slip prevails and similar microstructures are formed regardless of the test temperature and the testing mode (TMF and isothermal, respectively). As a result, the stressstrain response in TMF tests can be assessed from the corresponding isothermal data. Wavy dislocation slip was found to determine the stress-strain behavior if the maximum test temperature exceeded 600 °C. Moreover, in TMF tests with a maximum test temperature of 650 °C, the dislocation arrangement formed in the high-temperature part of the hysteresis loop was found to be stable throughout the cycle and to affect significantly the stress-strain response at the low temperatures. Although in-phase (IP) and out-of-phase (OP) TMF tests led to an almost identical microstructure, OP loading was always found to be most detrimental. The interaction between the embrittled subsurface layer, caused by oxygen uptake, and the high tensile stresses developing in the low-temperature part of the hysteresis loop in OP tests eases crack initiation and initial crack propagation and results in reduced fatigue life.

ASJC Scopus Sachgebiete

Zitieren

Thermomechanical Fatigue Behavior of the High-Temperature Titanium Alloy IMI 834. / Pototzky, P.; Maier, H. J.; Christ, H. J. et al.
in: Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, Jahrgang 29, Nr. 12, 1998, S. 2995-3004.

Publikation: Beitrag in FachzeitschriftArtikelForschungPeer-Review

Download
@article{4f375b4b1b914f8994a60a6912ed92dd,
title = "Thermomechanical Fatigue Behavior of the High-Temperature Titanium Alloy IMI 834",
abstract = "The isothermal and thermomechanical fatigue (TMF) behavior of the titanium alloy IMI 834 was studied between 350 °C and 650 °C in air and vacuum, respectively. Transmission electron microscopy (TEM) observations revealed that the microstructure established in the TMF tests was governed by the maximum temperature within the cycle. However, if the maximum temperature does not exceed 600 °C, planar dislocation slip prevails and similar microstructures are formed regardless of the test temperature and the testing mode (TMF and isothermal, respectively). As a result, the stressstrain response in TMF tests can be assessed from the corresponding isothermal data. Wavy dislocation slip was found to determine the stress-strain behavior if the maximum test temperature exceeded 600 °C. Moreover, in TMF tests with a maximum test temperature of 650 °C, the dislocation arrangement formed in the high-temperature part of the hysteresis loop was found to be stable throughout the cycle and to affect significantly the stress-strain response at the low temperatures. Although in-phase (IP) and out-of-phase (OP) TMF tests led to an almost identical microstructure, OP loading was always found to be most detrimental. The interaction between the embrittled subsurface layer, caused by oxygen uptake, and the high tensile stresses developing in the low-temperature part of the hysteresis loop in OP tests eases crack initiation and initial crack propagation and results in reduced fatigue life.",
author = "P. Pototzky and Maier, {H. J.} and Christ, {H. J.} and P. Pototzky",
note = "Funding Information: Financial support of this study by Deutsche Forschungs-gemeinschaft is gratefully acknowledged.",
year = "1998",
doi = "10.1007/s11661-998-0207-x",
language = "English",
volume = "29",
pages = "2995--3004",
journal = "Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science",
issn = "1073-5623",
publisher = "Springer Boston",
number = "12",

}

Download

TY - JOUR

T1 - Thermomechanical Fatigue Behavior of the High-Temperature Titanium Alloy IMI 834

AU - Pototzky, P.

AU - Maier, H. J.

AU - Christ, H. J.

AU - Pototzky, P.

N1 - Funding Information: Financial support of this study by Deutsche Forschungs-gemeinschaft is gratefully acknowledged.

PY - 1998

Y1 - 1998

N2 - The isothermal and thermomechanical fatigue (TMF) behavior of the titanium alloy IMI 834 was studied between 350 °C and 650 °C in air and vacuum, respectively. Transmission electron microscopy (TEM) observations revealed that the microstructure established in the TMF tests was governed by the maximum temperature within the cycle. However, if the maximum temperature does not exceed 600 °C, planar dislocation slip prevails and similar microstructures are formed regardless of the test temperature and the testing mode (TMF and isothermal, respectively). As a result, the stressstrain response in TMF tests can be assessed from the corresponding isothermal data. Wavy dislocation slip was found to determine the stress-strain behavior if the maximum test temperature exceeded 600 °C. Moreover, in TMF tests with a maximum test temperature of 650 °C, the dislocation arrangement formed in the high-temperature part of the hysteresis loop was found to be stable throughout the cycle and to affect significantly the stress-strain response at the low temperatures. Although in-phase (IP) and out-of-phase (OP) TMF tests led to an almost identical microstructure, OP loading was always found to be most detrimental. The interaction between the embrittled subsurface layer, caused by oxygen uptake, and the high tensile stresses developing in the low-temperature part of the hysteresis loop in OP tests eases crack initiation and initial crack propagation and results in reduced fatigue life.

AB - The isothermal and thermomechanical fatigue (TMF) behavior of the titanium alloy IMI 834 was studied between 350 °C and 650 °C in air and vacuum, respectively. Transmission electron microscopy (TEM) observations revealed that the microstructure established in the TMF tests was governed by the maximum temperature within the cycle. However, if the maximum temperature does not exceed 600 °C, planar dislocation slip prevails and similar microstructures are formed regardless of the test temperature and the testing mode (TMF and isothermal, respectively). As a result, the stressstrain response in TMF tests can be assessed from the corresponding isothermal data. Wavy dislocation slip was found to determine the stress-strain behavior if the maximum test temperature exceeded 600 °C. Moreover, in TMF tests with a maximum test temperature of 650 °C, the dislocation arrangement formed in the high-temperature part of the hysteresis loop was found to be stable throughout the cycle and to affect significantly the stress-strain response at the low temperatures. Although in-phase (IP) and out-of-phase (OP) TMF tests led to an almost identical microstructure, OP loading was always found to be most detrimental. The interaction between the embrittled subsurface layer, caused by oxygen uptake, and the high tensile stresses developing in the low-temperature part of the hysteresis loop in OP tests eases crack initiation and initial crack propagation and results in reduced fatigue life.

UR - http://www.scopus.com/inward/record.url?scp=0032292675&partnerID=8YFLogxK

U2 - 10.1007/s11661-998-0207-x

DO - 10.1007/s11661-998-0207-x

M3 - Article

AN - SCOPUS:0032292675

VL - 29

SP - 2995

EP - 3004

JO - Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science

JF - Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science

SN - 1073-5623

IS - 12

ER -

Von denselben Autoren