| Titel in Übersetzung | Low-temperature fatigue-induced martensitic transformation of a metastable austenitic stainless steel: Optimization of strength and fatigue properties |
|---|---|
| Originalsprache | Deutsch |
| Seiten (von - bis) | 820-826 |
| Seitenumfang | 7 |
| Fachzeitschrift | Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques |
| Jahrgang | 84 |
| Ausgabenummer | 12 |
| Publikationsstatus | Veröffentlicht - Dez. 1993 |
| Extern publiziert | Ja |
Abstract
The enhancement of the strength of a metastable austenitic AISI 304 L-type stainless steel by fatigue-induced martensite formation in the temperature range 103 K to 298 K was investigated. The fatigue tests were run in closed-loop plastic strain control using a symmetric sinusoidal wave form (0.2 Hz). Plastic strain amplitudes were in the range 3.2×10-3 to 1.26×10-2. The increase in strength caused by fatigue-induced martensite formation was measured by subsequent monotonic tensile tests at room temperature. The fatigue-induced martensite content and, as a consequence, the increase in strength and the residual fatigue life vary strongly with pre-deformation conditions (plastic strain range, test temperature, number of cycles). The cyclic pre-deformation conditions can be optimized to achieve the best combination of strength and residual fatigue life as required for technical applications.
ASJC Scopus Sachgebiete
- Physik und Astronomie (insg.)
- Physik der kondensierten Materie
- Chemie (insg.)
- Physikalische und Theoretische Chemie
- Werkstoffwissenschaften (insg.)
- Metalle und Legierungen
- Werkstoffwissenschaften (insg.)
- Werkstoffchemie
Zitieren
- Standard
- Harvard
- Apa
- Vancouver
- BibTex
- RIS
in: Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques, Jahrgang 84, Nr. 12, 12.1993, S. 820-826.
Publikation: Beitrag in Fachzeitschrift › Artikel › Forschung › Peer-Review
}
TY - JOUR
T1 - Optimierte Festigkeitssteigerung eines metastabilen austenitischen Stahles durch wechselverformungsinduzierte Martensitumwandlung bei tiefen Temperaturen
AU - Maier, Hans Juergen
AU - Donth, Bernhard
AU - Bayerlein, Manfred
AU - Mughrabi, Haeel
AU - Meier, Birgin
AU - Kesten, Martin
PY - 1993/12
Y1 - 1993/12
N2 - The enhancement of the strength of a metastable austenitic AISI 304 L-type stainless steel by fatigue-induced martensite formation in the temperature range 103 K to 298 K was investigated. The fatigue tests were run in closed-loop plastic strain control using a symmetric sinusoidal wave form (0.2 Hz). Plastic strain amplitudes were in the range 3.2×10-3 to 1.26×10-2. The increase in strength caused by fatigue-induced martensite formation was measured by subsequent monotonic tensile tests at room temperature. The fatigue-induced martensite content and, as a consequence, the increase in strength and the residual fatigue life vary strongly with pre-deformation conditions (plastic strain range, test temperature, number of cycles). The cyclic pre-deformation conditions can be optimized to achieve the best combination of strength and residual fatigue life as required for technical applications.
AB - The enhancement of the strength of a metastable austenitic AISI 304 L-type stainless steel by fatigue-induced martensite formation in the temperature range 103 K to 298 K was investigated. The fatigue tests were run in closed-loop plastic strain control using a symmetric sinusoidal wave form (0.2 Hz). Plastic strain amplitudes were in the range 3.2×10-3 to 1.26×10-2. The increase in strength caused by fatigue-induced martensite formation was measured by subsequent monotonic tensile tests at room temperature. The fatigue-induced martensite content and, as a consequence, the increase in strength and the residual fatigue life vary strongly with pre-deformation conditions (plastic strain range, test temperature, number of cycles). The cyclic pre-deformation conditions can be optimized to achieve the best combination of strength and residual fatigue life as required for technical applications.
UR - http://www.scopus.com/inward/record.url?scp=0027866761&partnerID=8YFLogxK
M3 - Artikel
AN - SCOPUS:0027866761
VL - 84
SP - 820
EP - 826
JO - Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques
JF - Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques
SN - 0044-3093
IS - 12
ER -