Abstract
Manufacturing of microstructured functional surfaces on components has become the focus of many research works in recent years. Based on traditional machining technologies, micromachining technologies have been further developed to produce microstructures. In this paper, the grinding process was investigated for the surface microstructuring at the example of riblet structures. The in streamwise direction aligned micro ribs (riblets) can reduce the near-wall turbulent surface friction up to 10% compared with smooth surfaces. The accomplished experiments show that by applying vitrified grinding wheels with micro profile tips generated by form dressing, microgroove structures with a width of 60 μm and depth of 20 μm can be manufactured for large area surfaces sufficiently. Both conventional SiC and superhard cBN grinding wheels were investigated concerning the profile accuracy during dressing and holding behaviour at grinding. The fabricated microstructures have been analysed concerning material removal and profile formation mechanisms.
ASJC Scopus Sachgebiete
- Werkstoffwissenschaften (insg.)
- Allgemeine Materialwissenschaften
- Ingenieurwesen (insg.)
- Werkstoffmechanik
- Ingenieurwesen (insg.)
- Maschinenbau
- Ingenieurwesen (insg.)
- Wirtschaftsingenieurwesen und Fertigungstechnik
Zitieren
- Standard
- Harvard
- Apa
- Vancouver
- BibTex
- RIS
in: International Journal of Abrasive Technology, Jahrgang 2, Nr. 2, 21.01.2009, S. 207-222.
Publikation: Beitrag in Fachzeitschrift › Artikel › Forschung › Peer-Review
}
TY - JOUR
T1 - Manufacturing of functional microstructured surfaces by grinding with vitrified SiC- and cBN-wheels
AU - Denkena, Berend
AU - Boehnke, David
AU - Wang, Bo
PY - 2009/1/21
Y1 - 2009/1/21
N2 - Manufacturing of microstructured functional surfaces on components has become the focus of many research works in recent years. Based on traditional machining technologies, micromachining technologies have been further developed to produce microstructures. In this paper, the grinding process was investigated for the surface microstructuring at the example of riblet structures. The in streamwise direction aligned micro ribs (riblets) can reduce the near-wall turbulent surface friction up to 10% compared with smooth surfaces. The accomplished experiments show that by applying vitrified grinding wheels with micro profile tips generated by form dressing, microgroove structures with a width of 60 μm and depth of 20 μm can be manufactured for large area surfaces sufficiently. Both conventional SiC and superhard cBN grinding wheels were investigated concerning the profile accuracy during dressing and holding behaviour at grinding. The fabricated microstructures have been analysed concerning material removal and profile formation mechanisms.
AB - Manufacturing of microstructured functional surfaces on components has become the focus of many research works in recent years. Based on traditional machining technologies, micromachining technologies have been further developed to produce microstructures. In this paper, the grinding process was investigated for the surface microstructuring at the example of riblet structures. The in streamwise direction aligned micro ribs (riblets) can reduce the near-wall turbulent surface friction up to 10% compared with smooth surfaces. The accomplished experiments show that by applying vitrified grinding wheels with micro profile tips generated by form dressing, microgroove structures with a width of 60 μm and depth of 20 μm can be manufactured for large area surfaces sufficiently. Both conventional SiC and superhard cBN grinding wheels were investigated concerning the profile accuracy during dressing and holding behaviour at grinding. The fabricated microstructures have been analysed concerning material removal and profile formation mechanisms.
KW - Functional surface
KW - Microstructuring
KW - Profile grinding
KW - Riblets
UR - http://www.scopus.com/inward/record.url?scp=78649443668&partnerID=8YFLogxK
U2 - 10.1504/IJAT.2009.022588
DO - 10.1504/IJAT.2009.022588
M3 - Article
AN - SCOPUS:78649443668
VL - 2
SP - 207
EP - 222
JO - International Journal of Abrasive Technology
JF - International Journal of Abrasive Technology
SN - 1752-2641
IS - 2
ER -