Abstract
Carbon-fibre reinforced plastics (CFRP) and glass-fibre reinforced plastics (GFRP) are widely used for components in the aviation and wind energy industries and suffer from damages or wear during operation. As soon as automobiles containing CFRP parts will go into large batch production and enter the market in the near future, the need for reliable repair and post-production processes will increase. One step in such a repair chain or post process can be nanosecond(ns)-pulsed UV-laser macro-structuring to prepare damaged surfaces for a composite bonded repair. It is important for a bonded repair that machined areas exhibit sufficient wettability for an adhesive to achieve optimal distribution on the substrate in order to sustain high shear strength. In this article several combinations of laser and process parameters will be investigated regarding the processability of glass- and carbon-fibre reinforced epoxy of unidirectional (UD) ply build up. The processability will be evaluated by measuring the surface roughness and the contact angle to predict the wettability of the surfaces. The evaluated parameter sets will be used to process bonded butt lap joint coupons for shear strength tests, in order to verify the suitability of laser processes for a bonded repair strategy of composites.
ASJC Scopus Sachgebiete
- Werkstoffwissenschaften (insg.)
- Elektronische, optische und magnetische Materialien
Zitieren
- Standard
- Harvard
- Apa
- Vancouver
- BibTex
- RIS
2013. 546-553 Beitrag in 32nd International Congress on Applications of Lasers and Electro-Optics, ICALEO 2013, Miami, FL, USA / Vereinigte Staaten.
Publikation: Konferenzbeitrag › Paper › Forschung › Peer-Review
}
TY - CONF
T1 - Macro-structuring of composite material by uv-laser ablation
AU - Dittmar, Hagen
AU - Jaeschke, Peter
AU - Suttmann, Oliver
AU - Overmeyer, Ludger
PY - 2013
Y1 - 2013
N2 - Carbon-fibre reinforced plastics (CFRP) and glass-fibre reinforced plastics (GFRP) are widely used for components in the aviation and wind energy industries and suffer from damages or wear during operation. As soon as automobiles containing CFRP parts will go into large batch production and enter the market in the near future, the need for reliable repair and post-production processes will increase. One step in such a repair chain or post process can be nanosecond(ns)-pulsed UV-laser macro-structuring to prepare damaged surfaces for a composite bonded repair. It is important for a bonded repair that machined areas exhibit sufficient wettability for an adhesive to achieve optimal distribution on the substrate in order to sustain high shear strength. In this article several combinations of laser and process parameters will be investigated regarding the processability of glass- and carbon-fibre reinforced epoxy of unidirectional (UD) ply build up. The processability will be evaluated by measuring the surface roughness and the contact angle to predict the wettability of the surfaces. The evaluated parameter sets will be used to process bonded butt lap joint coupons for shear strength tests, in order to verify the suitability of laser processes for a bonded repair strategy of composites.
AB - Carbon-fibre reinforced plastics (CFRP) and glass-fibre reinforced plastics (GFRP) are widely used for components in the aviation and wind energy industries and suffer from damages or wear during operation. As soon as automobiles containing CFRP parts will go into large batch production and enter the market in the near future, the need for reliable repair and post-production processes will increase. One step in such a repair chain or post process can be nanosecond(ns)-pulsed UV-laser macro-structuring to prepare damaged surfaces for a composite bonded repair. It is important for a bonded repair that machined areas exhibit sufficient wettability for an adhesive to achieve optimal distribution on the substrate in order to sustain high shear strength. In this article several combinations of laser and process parameters will be investigated regarding the processability of glass- and carbon-fibre reinforced epoxy of unidirectional (UD) ply build up. The processability will be evaluated by measuring the surface roughness and the contact angle to predict the wettability of the surfaces. The evaluated parameter sets will be used to process bonded butt lap joint coupons for shear strength tests, in order to verify the suitability of laser processes for a bonded repair strategy of composites.
UR - http://www.scopus.com/inward/record.url?scp=84893032702&partnerID=8YFLogxK
U2 - 10.2351/1.5062929
DO - 10.2351/1.5062929
M3 - Paper
AN - SCOPUS:84893032702
SP - 546
EP - 553
T2 - 32nd International Congress on Applications of Lasers and Electro-Optics, ICALEO 2013
Y2 - 6 October 2013 through 10 October 2013
ER -