Details
| Originalsprache | Englisch |
|---|---|
| Titel des Sammelwerks | Lecture Notes in Production Engineering |
| Herausgeber (Verlag) | Springer Nature |
| Seiten | 125-133 |
| Seitenumfang | 9 |
| Publikationsstatus | Veröffentlicht - 2021 |
| Veranstaltung | 10th Congress of the German Academic Association for Production Technology (WGP) - Dresden, Deutschland Dauer: 23 Sept. 2020 → 24 Sept. 2020 |
Publikationsreihe
| Name | Lecture Notes in Production Engineering |
|---|---|
| Band | Part F1136 |
| ISSN (Print) | 2194-0525 |
| ISSN (elektronisch) | 2194-0533 |
Abstract
From a metal forming perspective, warm forming technologies can be used to reclaim the shape and functionality of worn engineering steel parts such as case-hardened geared components. Since forming temperatures are beneath the material-transformation temperature, no loss in hardness is expected and a new heat treatment can be omitted. In order to determine a process window for reclaiming geared components, upsetting tests were carried out on case-hardened workpieces made of AISI 5115. The workpieces were heated to between 700 °C and 900 °C by induction or furnace heating and upset to a true strain between 0.1 and 0.4. The upset workpieces were cooled in two media, air and water, and metallographically investigated. The combination of 900 °C furnace heating, upsetting (φh = 0.4) and quenching led to an increase of 60% in case-hardening depth. This procedure can be used for reclaiming geared components by means of forming technology.
ASJC Scopus Sachgebiete
- Ingenieurwesen (insg.)
- Wirtschaftsingenieurwesen und Fertigungstechnik
- Volkswirtschaftslehre, Ökonometrie und Finanzen (insg.)
- Volkswirtschaftslehre, Ökonometrie und Finanzen (sonstige)
- Ingenieurwesen (insg.)
- Sicherheit, Risiko, Zuverlässigkeit und Qualität
Zitieren
- Standard
- Harvard
- Apa
- Vancouver
- BibTex
- RIS
Lecture Notes in Production Engineering. Springer Nature, 2021. S. 125-133 (Lecture Notes in Production Engineering; Band Part F1136).
Publikation: Beitrag in Buch/Bericht/Sammelwerk/Konferenzband › Beitrag in Buch/Sammelwerk › Forschung › Peer-Review
}
TY - CHAP
T1 - Experimental Process Design for Reclamation of Geared Components
AU - Kuwert, P.
AU - Petersen, T.
AU - Brunotte, K.
AU - Behrens, B. A.
N1 - Funding Information: “Determination of the process limits for the re-manufacturing of damaged gears by using precision post-forming at elevated temperatures” which is financed by the German Research Foundation (DFG) under the project number 319564414. The authors would like to thank the German Research Foundation.
PY - 2021
Y1 - 2021
N2 - From a metal forming perspective, warm forming technologies can be used to reclaim the shape and functionality of worn engineering steel parts such as case-hardened geared components. Since forming temperatures are beneath the material-transformation temperature, no loss in hardness is expected and a new heat treatment can be omitted. In order to determine a process window for reclaiming geared components, upsetting tests were carried out on case-hardened workpieces made of AISI 5115. The workpieces were heated to between 700 °C and 900 °C by induction or furnace heating and upset to a true strain between 0.1 and 0.4. The upset workpieces were cooled in two media, air and water, and metallographically investigated. The combination of 900 °C furnace heating, upsetting (φh = 0.4) and quenching led to an increase of 60% in case-hardening depth. This procedure can be used for reclaiming geared components by means of forming technology.
AB - From a metal forming perspective, warm forming technologies can be used to reclaim the shape and functionality of worn engineering steel parts such as case-hardened geared components. Since forming temperatures are beneath the material-transformation temperature, no loss in hardness is expected and a new heat treatment can be omitted. In order to determine a process window for reclaiming geared components, upsetting tests were carried out on case-hardened workpieces made of AISI 5115. The workpieces were heated to between 700 °C and 900 °C by induction or furnace heating and upset to a true strain between 0.1 and 0.4. The upset workpieces were cooled in two media, air and water, and metallographically investigated. The combination of 900 °C furnace heating, upsetting (φh = 0.4) and quenching led to an increase of 60% in case-hardening depth. This procedure can be used for reclaiming geared components by means of forming technology.
KW - Bulk metal forming
KW - CO-reduction
KW - Product recycling
UR - http://www.scopus.com/inward/record.url?scp=85165973416&partnerID=8YFLogxK
U2 - 10.1007/978-3-662-62138-7_13
DO - 10.1007/978-3-662-62138-7_13
M3 - Contribution to book/anthology
AN - SCOPUS:85165973416
T3 - Lecture Notes in Production Engineering
SP - 125
EP - 133
BT - Lecture Notes in Production Engineering
PB - Springer Nature
T2 - 10th Congress of the German Academic Association for Production Technology (WGP)
Y2 - 23 September 2020 through 24 September 2020
ER -