Abstract
Calcium phosphates are widely present in geological and industrial settings and make up the majority of our bone’s inorganic content; however, their formation from solution is not fully understood. The nucleation of calcium phosphate phases was studied using a state-of-the-art titration setup. The effect of varied calcium addition rate was studied at a range of pH values between pH 7 and pH 8; the precipitated crystals were isolated and analyzed. Dicalcium phosphate dihydrate (DCPD) was formed at lower pH and a slow addition rate. Intermediate addition rates yielded a mix of DCPD and poorly crystalline hydroxyapatite (PC-HA). At fast addition rates and above pH 7.5, poorly crystalline hydroxyapatite was precipitated exclusively. The results indicate that counterintuitive kinetic effects play a substantial role in the nucleation of calcium phosphates.
ASJC Scopus Sachgebiete
- Chemie (insg.)
- Allgemeine Chemie
- Werkstoffwissenschaften (insg.)
- Allgemeine Materialwissenschaften
- Physik und Astronomie (insg.)
- Physik der kondensierten Materie
Zitieren
- Standard
- Harvard
- Apa
- Vancouver
- BibTex
- RIS
in: Crystal Growth and Design, Jahrgang 23, Nr. 10, 04.10.2023, S. 7037–7043.
Publikation: Beitrag in Fachzeitschrift › Artikel › Forschung › Peer-Review
}
TY - JOUR
T1 - Counterintuitive Crystallization
T2 - Rate Effects in Calcium Phosphate Nucleation at Near-Physiological pH
AU - McDonogh, David P.
AU - Kirupananthan, Priyanthan
AU - Gebauer, Denis
N1 - Funding Information: We would like to thank the cfMATCH analytics center at the Leibniz University Hannover for support and insight with the TEM measurements.
PY - 2023/10/4
Y1 - 2023/10/4
N2 - Calcium phosphates are widely present in geological and industrial settings and make up the majority of our bone’s inorganic content; however, their formation from solution is not fully understood. The nucleation of calcium phosphate phases was studied using a state-of-the-art titration setup. The effect of varied calcium addition rate was studied at a range of pH values between pH 7 and pH 8; the precipitated crystals were isolated and analyzed. Dicalcium phosphate dihydrate (DCPD) was formed at lower pH and a slow addition rate. Intermediate addition rates yielded a mix of DCPD and poorly crystalline hydroxyapatite (PC-HA). At fast addition rates and above pH 7.5, poorly crystalline hydroxyapatite was precipitated exclusively. The results indicate that counterintuitive kinetic effects play a substantial role in the nucleation of calcium phosphates.
AB - Calcium phosphates are widely present in geological and industrial settings and make up the majority of our bone’s inorganic content; however, their formation from solution is not fully understood. The nucleation of calcium phosphate phases was studied using a state-of-the-art titration setup. The effect of varied calcium addition rate was studied at a range of pH values between pH 7 and pH 8; the precipitated crystals were isolated and analyzed. Dicalcium phosphate dihydrate (DCPD) was formed at lower pH and a slow addition rate. Intermediate addition rates yielded a mix of DCPD and poorly crystalline hydroxyapatite (PC-HA). At fast addition rates and above pH 7.5, poorly crystalline hydroxyapatite was precipitated exclusively. The results indicate that counterintuitive kinetic effects play a substantial role in the nucleation of calcium phosphates.
UR - http://www.scopus.com/inward/record.url?scp=85175154997&partnerID=8YFLogxK
U2 - 10.1021/acs.cgd.3c00851
DO - 10.1021/acs.cgd.3c00851
M3 - Article
AN - SCOPUS:85175154997
VL - 23
SP - 7037
EP - 7043
JO - Crystal Growth and Design
JF - Crystal Growth and Design
SN - 1528-7483
IS - 10
ER -