Abstract
In the research of the compound forging of steel-aluminum parts mostly the upsetting test is used. In this paper the factors influencing the buckling behavior during the upsetting of mono hollow cylinders and hybrid steel-aluminum specimens are examined and characterized by two parameters. The buckle ratio is used as a measurement for the uniformity of the part geometry in radial direction and the buckle distance provides information about the part geometry in axial direction. The results gained by the upsetting of hollow cylinders show that the reproducibility depends on the wall thickness of the hollow steel cylinder. Above a forming temperature of T = 750 °C a transformation from mode II (double barrel profile) to mode I (single barrel profile) occurs. Furthermore, it could be shown, that the strain rate has no influence on the buckling behavior in both the upsetting of hollow cylinders as well as the upsetting of hybrid specimens. The results gained by the upsetting of hybrid steel aluminum specimens show that with increasing forming temperature the hybrid specimens with a wall thickness of the steel casing of s = 1 mm form more homogeneously in radial direction. In addition the scatter of the results decreases with increasing forming temperature.
ASJC Scopus Sachgebiete
- Ingenieurwesen (insg.)
- Maschinenbau
- Ingenieurwesen (insg.)
- Wirtschaftsingenieurwesen und Fertigungstechnik
Zitieren
- Standard
- Harvard
- Apa
- Vancouver
- BibTex
- RIS
in: Production Engineering, Jahrgang 7, Nr. 2-3, 17.01.2013, S. 167-176.
Publikation: Beitrag in Fachzeitschrift › Artikel › Forschung › Peer-Review
}
TY - JOUR
T1 - Characterizing the buckling behavior of cylindrical hollow and hybrid specimens by experimental upsetting tests
AU - Behrens, Bernd Arno
AU - Kosch, Klaus Georg
N1 - Funding information: Acknowledgments The presented research has been carried out within the research training groups 1378 ‘‘Manufacture, machining and qualification of hybrid material systems’’‘ sponsored by the German Research Foundation (DFG). We are thankful for the assistance provided.
PY - 2013/1/17
Y1 - 2013/1/17
N2 - In the research of the compound forging of steel-aluminum parts mostly the upsetting test is used. In this paper the factors influencing the buckling behavior during the upsetting of mono hollow cylinders and hybrid steel-aluminum specimens are examined and characterized by two parameters. The buckle ratio is used as a measurement for the uniformity of the part geometry in radial direction and the buckle distance provides information about the part geometry in axial direction. The results gained by the upsetting of hollow cylinders show that the reproducibility depends on the wall thickness of the hollow steel cylinder. Above a forming temperature of T = 750 °C a transformation from mode II (double barrel profile) to mode I (single barrel profile) occurs. Furthermore, it could be shown, that the strain rate has no influence on the buckling behavior in both the upsetting of hollow cylinders as well as the upsetting of hybrid specimens. The results gained by the upsetting of hybrid steel aluminum specimens show that with increasing forming temperature the hybrid specimens with a wall thickness of the steel casing of s = 1 mm form more homogeneously in radial direction. In addition the scatter of the results decreases with increasing forming temperature.
AB - In the research of the compound forging of steel-aluminum parts mostly the upsetting test is used. In this paper the factors influencing the buckling behavior during the upsetting of mono hollow cylinders and hybrid steel-aluminum specimens are examined and characterized by two parameters. The buckle ratio is used as a measurement for the uniformity of the part geometry in radial direction and the buckle distance provides information about the part geometry in axial direction. The results gained by the upsetting of hollow cylinders show that the reproducibility depends on the wall thickness of the hollow steel cylinder. Above a forming temperature of T = 750 °C a transformation from mode II (double barrel profile) to mode I (single barrel profile) occurs. Furthermore, it could be shown, that the strain rate has no influence on the buckling behavior in both the upsetting of hollow cylinders as well as the upsetting of hybrid specimens. The results gained by the upsetting of hybrid steel aluminum specimens show that with increasing forming temperature the hybrid specimens with a wall thickness of the steel casing of s = 1 mm form more homogeneously in radial direction. In addition the scatter of the results decreases with increasing forming temperature.
KW - Buckling
KW - Compound forging
KW - Hollow cylinder
KW - Hybrid part
KW - Massive forming
KW - Upsetting
UR - http://www.scopus.com/inward/record.url?scp=84875624638&partnerID=8YFLogxK
U2 - 10.1007/s11740-013-0445-7
DO - 10.1007/s11740-013-0445-7
M3 - Article
AN - SCOPUS:84875624638
VL - 7
SP - 167
EP - 176
JO - Production Engineering
JF - Production Engineering
SN - 0944-6524
IS - 2-3
ER -