Details
| Originalsprache | Englisch |
|---|---|
| Seiten (von - bis) | 17-29 |
| Seitenumfang | 13 |
| Fachzeitschrift | Journal of Biomaterials Applications |
| Jahrgang | 30 |
| Ausgabenummer | 1 |
| Publikationsstatus | Veröffentlicht - 6 Feb. 2015 |
Abstract
For several centuries silver is known for its antibacterial effects. The middle ear is an interesting new scope for silver application since chronic inflammations combined with bacterial infection cause complete destruction of the fragile ossicle chain and tympanic membrane. The resulting conductive deafness requires tympanoplasty for reconstruction. Strategies to prevent bacterial growth on middle ear prostheses are highly recommended. In this study, rabbits were implanted with Bioverit® II middle ear prostheses functionalized with silver containing dense and nanoporous silica films which were compared with pure silica coatings as well as silver sulfadiazine cream applied on nanoporous silica coating. The health status of animals was continuously monitored; blood was examined before and after implantation. After 21 days, the middle ears were inspected; implants and mucosal samples were processed for electron microscopy. Autopsies were performed and systemic spreading of silver was chemically analyzed exemplarily in liver and kidneys. For verification of direct cytotoxicity, NIH 3T3 cells were cultured on similar silver containing silica coatings on glass up to 3 days. In vitro a reduced viability of fibroblasts adhering directly on the samples was detected compared to cells growing on the surrounding plastic of the same culture dish. In transmission electron microscopy, phagocytosed silver silica fragments, silver sulfadiazine cream as well as silver nanoparticles were noticed inside endosomes. In vivo, clinical and post mortem examinations were inconspicuous. Chemical analyses showed no increased silver content compared to controls. Mucosal coverages on almost all prostheses were found. But reduction of granulation tissue was only obvious around silver-coated implants. Single necroses and apoptosis in the mucosa were correlated by intracellular accumulation of metallic silver. For confirming supportive healing effects of middle ear implants, silver ion aggregates need to be tested in the future to optimize biocompatibility while assuring bactericidal effects in the middle ear.
ASJC Scopus Sachgebiete
- Werkstoffwissenschaften (insg.)
- Biomaterialien
- Ingenieurwesen (insg.)
- Biomedizintechnik
Zitieren
- Standard
- Harvard
- Apa
- Vancouver
- BibTex
- RIS
in: Journal of Biomaterials Applications, Jahrgang 30, Nr. 1, 06.02.2015, S. 17-29.
Publikation: Beitrag in Fachzeitschrift › Artikel › Forschung › Peer-Review
}
TY - JOUR
T1 - Biocompatibility of silver containing silica films on Bioverit® II middle ear prostheses in rabbits
AU - Duda, Franziska
AU - Bradel, Susanne
AU - Bleich, André
AU - Abendroth, Philipp
AU - Heemeier, Tanja
AU - Ehlert, Nina
AU - Behrens, Peter
AU - Esser, Karl Heinz
AU - Lenarz, Thomas
AU - Brandes, Gudrun
AU - Prenzler, Nils K.
PY - 2015/2/6
Y1 - 2015/2/6
N2 - For several centuries silver is known for its antibacterial effects. The middle ear is an interesting new scope for silver application since chronic inflammations combined with bacterial infection cause complete destruction of the fragile ossicle chain and tympanic membrane. The resulting conductive deafness requires tympanoplasty for reconstruction. Strategies to prevent bacterial growth on middle ear prostheses are highly recommended. In this study, rabbits were implanted with Bioverit® II middle ear prostheses functionalized with silver containing dense and nanoporous silica films which were compared with pure silica coatings as well as silver sulfadiazine cream applied on nanoporous silica coating. The health status of animals was continuously monitored; blood was examined before and after implantation. After 21 days, the middle ears were inspected; implants and mucosal samples were processed for electron microscopy. Autopsies were performed and systemic spreading of silver was chemically analyzed exemplarily in liver and kidneys. For verification of direct cytotoxicity, NIH 3T3 cells were cultured on similar silver containing silica coatings on glass up to 3 days. In vitro a reduced viability of fibroblasts adhering directly on the samples was detected compared to cells growing on the surrounding plastic of the same culture dish. In transmission electron microscopy, phagocytosed silver silica fragments, silver sulfadiazine cream as well as silver nanoparticles were noticed inside endosomes. In vivo, clinical and post mortem examinations were inconspicuous. Chemical analyses showed no increased silver content compared to controls. Mucosal coverages on almost all prostheses were found. But reduction of granulation tissue was only obvious around silver-coated implants. Single necroses and apoptosis in the mucosa were correlated by intracellular accumulation of metallic silver. For confirming supportive healing effects of middle ear implants, silver ion aggregates need to be tested in the future to optimize biocompatibility while assuring bactericidal effects in the middle ear.
AB - For several centuries silver is known for its antibacterial effects. The middle ear is an interesting new scope for silver application since chronic inflammations combined with bacterial infection cause complete destruction of the fragile ossicle chain and tympanic membrane. The resulting conductive deafness requires tympanoplasty for reconstruction. Strategies to prevent bacterial growth on middle ear prostheses are highly recommended. In this study, rabbits were implanted with Bioverit® II middle ear prostheses functionalized with silver containing dense and nanoporous silica films which were compared with pure silica coatings as well as silver sulfadiazine cream applied on nanoporous silica coating. The health status of animals was continuously monitored; blood was examined before and after implantation. After 21 days, the middle ears were inspected; implants and mucosal samples were processed for electron microscopy. Autopsies were performed and systemic spreading of silver was chemically analyzed exemplarily in liver and kidneys. For verification of direct cytotoxicity, NIH 3T3 cells were cultured on similar silver containing silica coatings on glass up to 3 days. In vitro a reduced viability of fibroblasts adhering directly on the samples was detected compared to cells growing on the surrounding plastic of the same culture dish. In transmission electron microscopy, phagocytosed silver silica fragments, silver sulfadiazine cream as well as silver nanoparticles were noticed inside endosomes. In vivo, clinical and post mortem examinations were inconspicuous. Chemical analyses showed no increased silver content compared to controls. Mucosal coverages on almost all prostheses were found. But reduction of granulation tissue was only obvious around silver-coated implants. Single necroses and apoptosis in the mucosa were correlated by intracellular accumulation of metallic silver. For confirming supportive healing effects of middle ear implants, silver ion aggregates need to be tested in the future to optimize biocompatibility while assuring bactericidal effects in the middle ear.
KW - drug release system
KW - electron microscopy
KW - nanoporous silica
KW - silver ions
KW - Total ossicular chain reconstructive prosthesis
UR - http://www.scopus.com/inward/record.url?scp=84930858219&partnerID=8YFLogxK
U2 - 10.1177/0885328215570103
DO - 10.1177/0885328215570103
M3 - Article
C2 - 25659947
AN - SCOPUS:84930858219
VL - 30
SP - 17
EP - 29
JO - Journal of Biomaterials Applications
JF - Journal of Biomaterials Applications
SN - 0885-3282
IS - 1
ER -