Abstract
beta -active **1**1**0Ag nuclei have been produced in AgF, AgCl, AgBr by capture of polarized thermal neutrons. The capture process produces point defects which have been studied. Analysis of the NMR line shape showed that 30-40% of the **1**1**0Ag nuclei have undisturbed lattice whereas 60-70% have Ag** plus vacancies and interstitials. In the case of AgCl and AgBr, defect annealing was oberved in the temperature range 10-25 K.
ASJC Scopus Sachgebiete
- Ingenieurwesen (insg.)
- Allgemeiner Maschinenbau
Zitieren
- Standard
- Harvard
- Apa
- Vancouver
- BibTex
- RIS
in: Radiation Effects, Jahrgang 73, Nr. 1-4, 1983, S. 95-101.
Publikation: Beitrag in Fachzeitschrift › Konferenzaufsatz in Fachzeitschrift › Forschung › Peer-Review
}
TY - JOUR
T1 - ANNEALING OF (n, GAMMA) INDUCED POINT DEFECTS IN THE SILVER HALIDES.
AU - Stoeckmann, H. J.
AU - Doerr, K.
AU - Ackermann, H.
AU - Bader, B.
AU - Buttler, W.
AU - Freilaender, P.
AU - Grupp, H.
AU - Heitjans, P.
AU - Kiese, G.
N1 - Funding Information: This work was sponsored by the Bundesministerium fur Forschung und Technologie.
PY - 1983
Y1 - 1983
N2 - beta -active **1**1**0Ag nuclei have been produced in AgF, AgCl, AgBr by capture of polarized thermal neutrons. The capture process produces point defects which have been studied. Analysis of the NMR line shape showed that 30-40% of the **1**1**0Ag nuclei have undisturbed lattice whereas 60-70% have Ag** plus vacancies and interstitials. In the case of AgCl and AgBr, defect annealing was oberved in the temperature range 10-25 K.
AB - beta -active **1**1**0Ag nuclei have been produced in AgF, AgCl, AgBr by capture of polarized thermal neutrons. The capture process produces point defects which have been studied. Analysis of the NMR line shape showed that 30-40% of the **1**1**0Ag nuclei have undisturbed lattice whereas 60-70% have Ag** plus vacancies and interstitials. In the case of AgCl and AgBr, defect annealing was oberved in the temperature range 10-25 K.
UR - http://www.scopus.com/inward/record.url?scp=0020151480&partnerID=8YFLogxK
U2 - 10.1080/00337578308220660
DO - 10.1080/00337578308220660
M3 - Conference article
AN - SCOPUS:0020151480
VL - 73
SP - 95
EP - 101
JO - Radiation Effects
JF - Radiation Effects
SN - 0033-7579
IS - 1-4
T2 - Europhys Top Conf on Lattice Defects in Ionic Cryst, 4th, Pt B
Y2 - 29 August 1982 through 3 September 1982
ER -